Preparation of Semipermeable polyvinylpyrrolidone Membranes and Study Their Chemical, Physical and Mechanical Properties

تحضير أغشية نصف نفوذة من بولي فينيل بيروليدون ودراسة خواصها الكيميائية والفيزيائية والميكانيكية

المؤلفون

  • Khatoon Khalil Al-Hamad, Fawaz Ahmad Al- Deri, Ahmad Mohamd Al-Falah

الكلمات المفتاحية:

غشاء نصف نفوذ من بولي فينيل بيروليدون
طريقة تحول الحالة

الملخص

Been we had prepared three semipermeable membranes with different concentration of polyvinylpyrrolidone by the phase inversion process. This way is a basic method to get flat membranes. the membranes were tested for chemical properties (pH rang), and physical properties (viscosity and porosity), and mechanical properties (tensile strength and strain), The results showed that polyvinylpyrrolidone (8%, 12%,15%) membrane having the higher pH range, while the polyvinylpyrrolidone (15%) membrane having the higher tensile strength and strain, but it was having the lowest porosity, viscosity was measured in low concentration was showed that polyvinylpyrrolidone (2%) solution having the higher viscosity.

السيرة الشخصية للمؤلف

Khatoon Khalil Al-Hamad, Fawaz Ahmad Al- Deri, Ahmad Mohamd Al-Falah

 

Faculty of Sciences || Damascus University || Syria

التنزيلات

منشور

2020-12-30

كيفية الاقتباس

1.
Khatoon Khalil Al-Hamad, Fawaz Ahmad Al- Deri, Ahmad Mohamd Al-Falah. Preparation of Semipermeable polyvinylpyrrolidone Membranes and Study Their Chemical, Physical and Mechanical Properties: تحضير أغشية نصف نفوذة من بولي فينيل بيروليدون ودراسة خواصها الكيميائية والفيزيائية والميكانيكية. jnslas [انترنت]. 30 ديسمبر، 2020 [وثق 6 ديسمبر، 2021];4(4):31-22. موجود في: https://journals.ajsrp.com/index.php/jnslas/article/view/3154

إصدار

القسم

المقالات